Objective To study whether SiO2 films will influence the color of Ni-Cr metal ceramic restorations. Methods For the film plating experimental group, Sol-gel method was employed to apply SiO2 films to the surface of the Ni-Cr copings, while no coating was applied for the non-film-plating control group. Veneering porcelains were then applied subsequently, and a total of 12 B2-colored maxillary incisor metal ceramic crowns were fabricated with 6 crowns in each group. A ShadeEye Ncc computer-aided colorimeter was employed to measure the shade of the samples, as well as 6 B2（Vitapan classical vita color tabs） shade standards. The color was expressed as CIE-1976-Lab coordinates. Results There was a statistically significant color difference between all metal ceramic crowns and the B2 shade standards（ΔE>1.5）. The L*, a*, b* values of all crowns were higher than those of the B2 shade standards, and the crowns were typically yellower or redder. While neither significant color difference nor difference in shade values was observed between the film plating experimental group and non-film-plating control group（ΔE