Objective To investigate the variation of the corrosion resistance of anodized oxidation film on titanium by electrochemical methods. Methods TiO2 nanotube layer was formed on Ti surface by anodization. The morphology was observed with scanning electron microscope（SEM） and the crystal phase was analyzed using X-ray diffraction（XRD） before and after annealing． Polarization curves were examined by electrochemical methods. Results Titanium oxide nanotubes with 80 nm diameter and 400 nm length was seen on Ti after anodization. The annealing nanotubes was anatase crystalline phase by X-ray diffraction analysis. The self-corrosion potential and break-down potential of smooth Ti were significantly lower than TiO2 nanotubes by anodization（P