ObjectiveThis study aims to evaluate the differences in shear bond strength, marginal adaptation, and nano-microleakage after aging among snowplow, layered filling, and lining techniques applied to the resin-bonded restoration of defective primary teeth.MethodsIn this study, 51 freshly extracted, crown-intact primary anterior teeth and 30 primary molars were collected. The experimental groups were as follows: layered filling group, lining group, and snowplow group. Experiments were performed to compare the differences in shear bond strength, marginal integrity, and silver ion nano-microleakage after aging among these groups.ResultsThe median shear bond strength of the layered filling group, lining group, and snowplow group were 2.45, 5.72, and 9.43 MPa, respectively. The values for lining group and snowplow group were significantly higher than that for layered filling group (P<0 .05). no statistically significant difference was found between lining group and snowplow group (P>0.05). The median overall margin integrity of the layered filling group, lining group, and snowplow group were 55.38%, 48.25%, and 65.63%, respectively. The difference among the three groups was not statistically significant (P>0.05). The median percentages of silver ion nano-microleakage in the layered filling group, lining group, and snowplow group were 11.71%, 9.47%, and 11.55%, respectively. The difference among the three groups was not statistically significant (P>0.05).ConclusionApplying the snowplow technique to restore defective primary teeth can improve the bond strength and margin integrity and reduce nano-microleakage.